From: Genetic variation in Pinus taeda wood properties predicted using non-destructive techniques
Ā | GCA | SE | t | SCA | SE | GE | SE | Error | SE |
---|---|---|---|---|---|---|---|---|---|
Trait | GA diallel | ||||||||
Acoustic velocity | 288 | 144 | 2.0 | 0 | ā | 64 | 40 | 816 | 57 |
D. stiffness | 0.29 | 0.13 | 2.2 | 0 | ā | 0.02 | 0.02 | 0.73 | 0.05 |
NIR density | 201 | 102 | 2.0 | 0 | ā | 0 | ā | 810 | 100 |
NIR coarseness | 90 | 48 | 1.9 | 0 | ā | 0 | ā | 465 | 57 |
NIR MFA | 0.51 | 0.45 | 1.1 | 0.83 | 0.68 | 0.08 | 0.23 | 4.9 | 0.68 |
NIR MOE | 0.09 | 0.10 | 0.9 | 0.20 | 0.15 | 0.02 | 0.05 | 0.97 | 0.14 |
NIR cell wall | 0.004 | 0.002 | 2.0 | 0.0003 | 0.002 | 0.001 | 0.001 | 0.03 | 0.01 |
Ā | NC diallel | ||||||||
Acoustic velocity | 73 | 36 | 2.0 | 2.6 | 21 | 0 | ā | 579 | 39 |
D. stiffness | 0.17 | 0.08 | 2.1 | 0 | ā | 0 | ā | 1.3 | 0.1 |
NIR density | 593 | 278 | 2.1 | 0 | ā | 0 | ā | 1407 | 156 |
NIR coarseness | 136 | 72 | 1.9 | 0 | ā | 0 | ā | 825 | 92 |
NIR MFA | 0.34 | 0.25 | 1.4 | 0 | ā | 0 | ā | 6.6 | 0.7 |
NIR MOE | 0.30 | 0.17 | 1.8 | 0 | ā | 0 | ā | 2.3 | 0.3 |
NIR cell wall | 0.016 | 0.008 | 2.0 | 0 | ā | 0 | ā | 0.05 | 0.01 |
Ā | SC diallel | ||||||||
Acoustic velocity | 53 | 28 | 1.9 | 5.2 | 19 | 0 | ā | 598 | 40 |
D. stiffness | 0.1 | 0.05 | 2.0 | 0 | ā | 0 | ā | 1.2 | 0.07 |
NIR density | 167 | 91 | 1.8 | 0 | ā | 5 | 36 | 982 | 112 |
NIR coarseness | 17 | 23 | 0.7 | 0 | ā | 31 | 26 | 377 | 43 |
NIR MFA | 0.45 | 0.31 | 1.5 | 0 | ā | 0.05 | 0.19 | 5.4 | 0.62 |
NIR MOE | 0.10 | 0.08 | 1.3 | 0 | ā | 0.05 | 0.06 | 1.3 | 0.1 |
NIR cell wall | 0.002 | 0.002 | 1.0 | 0 | ā | 0.002 | 0.002 | 0.03 | 0.003 |