Traita | Trial | Mean | Rangeb | \( {\widehat{h}}^2 \) | \( {\widehat{P}}^2 \) | |
---|---|---|---|---|---|---|
Min | Max | |||||
Diameter (cm) | Pleiku | 16.8 (0.2) | 10.8 | 25.5 | 0.14 (0.08) | 0.01 (0.02) |
Bau Bang | 21.0 (0.3) | 9.3 | 34 | 0.33 (0.11) | 0.04 (0.04) | |
Density (kg/m3) | Pleiku | 657 (3) | 554 | 829 | 0.23 (0.13) | 0.04 (0.04) |
Bau Bang | 665 (3) | 569 | 779 | 0.25 (0.10) | 0.05 (0.04) | |
Kraft pulp yield (%) | Pleiku | 46.8 (0.1) | 42.6 | 51.7 | 0.29 (0.14) | 0.03 (0.02) |
Bau Bang | 45.5 (0.2) | 39.3 | 50.3 | 0.47 (0.13) | 0.11 (0.07) | |
Modulus of elasticity (GPa) | Pleiku | 19.0 (0.2) | 13.3 | 27 | 0.36 (0.14) | 0.03 (0.03) |
Bau Bang | 19.5 (0.2) | 13.6 | 29.5 | 0.51 (0.14) | 0.10 (0.07) | |
Microfibril angle (°) | Pleiku | 15.1 (0.1) | 11 | 18.7 | 0.14 (0.12) | 0.02 (0.02) |
Bau Bang | 14.5 (0.2) | 9 | 19 | 0.48 (0.13) | 0.10 (0.06) |